UV10LVDC

硕士邦德UV10LVDC是一个新的组成部分紫外线和/或热固化改性环氧粘接性能高，涂料，树脂浇注应用系统。 当暴露在紫外线光或热，UV10LVDC容易治愈源强耐化学腐蚀的债券，涂料或铸件。 固化后的UV10LVDC化合物可用于在宽温度范围为-60 ° F至300 ° F。 对于UV固化，最大吸收被发现在320-360纳米范围内。 治愈也可以是通过加热，在250 ° F约20分钟，在烤箱UV10LVDC化合物。 该硕士邦德UV10LVDC双重固化能力大大增强UV固化技术通过扩展其适用于光学组件包括两个不透明和透明的组件工具。 主键UV10LVDC氧树脂体系不抑制，不要求对紫外线或热固化或惰性气氛。 与大多数其他紫外线固化系统，UV10LVDC化合物可以在广泛的部分固化厚度达1 / 4“多，这大大增加了系统的实用性的UV10LVDC范围铸造和封装，以及粘合和涂层应用。保税组装，涂料和铸件长期耐用性极佳，即使暴露，包括高温，潮湿，化学品对环境的不利条件等硕士邦德UV10LVDC具有高物理强度和优越的耐化学性，无机化学品，包括酸，碱和盐以及有机化学品，如最常见的溶剂，高强度债券获得的金属，陶瓷，玻璃，造纸，许多塑料和弹性体的复合是100％反应，不含有任何溶剂或稀释剂。固化与最小的影响收缩。硕士邦德UV10LVDC的卓越性能配置，是由于其独特的化学组成，其中包括一个exceptinally有效的紫外线固化剂和卓越的热固化的催化剂。快速紫外光固化机制是通过接触市售200瓦特/线性英寸的中压汞触发蒸汽灯或类似设备，随着这种商业紫外线灯，治疗可以在非常短的时间内生效期间，如1分钟或在环境温度低，当低强度紫外线灯是采用较长的固化时间是必要的。如上所述，烤箱治疗可达到大约20分钟。在250 ° F的物理强度，耐化学性和完全治愈UV10LVDC化合物的方法由传统的环氧树脂系统展出的粘接性能。

Master Bond UV10LVDC is a new one component UV and/or heat curable modified epoxy resin system for high performance bonding, coating and casting applications. When exposed to a source of UV light or heat, UV10LVDC cures readily to strong chemically resistant bonds, coatings or castings. The cured UV10LVDC compound can be used over the wide temperature range of -60°F to 300°F. For UV curing, the maximum absorption is found in the 320-360 nanometer range. Cures can also be effected by heating the UV10LVDC compound in an oven at 250°F for approximately 20 minutes. The dual cure capability of the Master Bond UV10LVDC greatly enhances the utility of UV curing technology by extending its applicability to assemblies comprising both optically opaque and transparent components. The Master Bond UV10LVDC resin system is not oxygen inhibited and does not require an inert atmosphere for either UV or thermal cures. Unlike most other UV curing systems, the UV10LVDC compound can be cured in a wide range of section thicknesses up to 1/4″ and more. This greatly increases the range of usefulness of the UV10LVDC system to casting and encapsulation as well as bonding and coating applications. Long term durability of bonded assemblies, coatings and castings is excellent even when exposed to adverse environmental conditions including heat, moisture, chemicals, etc. Master Bond UV10LVDC exhibits high physical strength and superior chemical resistance to inorganic chemicals including acids, bases and salts as well as organic chemicals such as most common solvents. High strength bonds are obtained with metals, ceramics, glass, paper, many plastics and elastomers. The compound is 100% reactive and does not contain any solvents or diluents. Cures are effected with minimal shrinkage. Master Bond UV10LVDC’s superior performance profile is due to its unique chemical composition which includes an exceptinally effective UV curing agent and a superior thermally curing catalyst. The fast UV curing mechanism is triggered by exposure to commercially available 200 watt/linear inch medium pressure mercury vapor lamps or similar equipment. With such commercial UV lamps, cures can be effected in remarkably short time periods, e.g., 1 minute or less at ambient temperatures. When lower intensity UV lamps are employed somewhat longer curing times are necessary. As noted, oven cures can be achieved at 250°F in approximately 20 minutes. The physical strength, chemical resistance and adhesive properties of the fully cured UV10LVDC compound approach those exhibited by conventional epoxy resin systems.