| Transmission Range % | 50 |
| Transmission Range | 0.2 – 6.2 µm (Thickness 1/0.4 mm) |
| Refractive Index | 1.829452 @633 nm |
| Reflection Loss | 7.9% @3µm |
| Density | 4.56 g/cm3 |
| Melting point | 1950°C |
| Molecular Weight | 593.62 |
| Thermal Conductivity | 13.1 W/(m·K) |
| Spec. Heat Capacity | 628 J/(kg·K) |
| Thermal Expansion | 7.5 · 10-6/K @300K) |
| Hardness (Mohs) | 1350 (Indenter Load 200g) |
| Young’s Modulus | 280 GPa |
| Shear Modulus | 113 GPa |
| Bulk Modulus | 180 GPa |
| Fracture Modulus | 250 MPa |
| Elastic Coefficient | C11 = 333; C12 = 111; C44 = 114 GPa |
| Dielectric Constant | 7.75 @298K |
| Solubility in Water | none |
| Crystal Structure | single crystal, synthetic |
| Crystal Type | cubic |
| Lattice Constants | a = 12.008 Å |
| Orientation | 111, 100 |
| Poisson Ratio | 0.24 |
| Application | active laser crystals (dopants: Nd, Tm, Ho, Er, Cr), spectroscopy, vacuum windows, IR optics |
Alkali Halides Barium Fluoride氟化钡 Barium Fluoride 氟化钡 Caesium Iodide 碘化铯 Calcium Fluoride氟化钙 Calcium Fluoride 氟化钙 Crystal Growth Fused Silica 熔融二氧化硅 Germanium 锗 II-VI-Compounds KRS-5 KRS-5 KRS-5 KRS-5 KRS-5型 KRS-6 Lanthan Fluoride 氟化镧 Lead Fluoride 氟化铅 Lithium Fluoride 氟化锂 Magnesium Fluoride 氟化镁 Oxide crystals Potassium Bromide 溴化钾 Potassium Chloride 氯化钾 Potassium Iodide 碘化钾 Quartz crystalline 石英晶体 Sapphire 蓝宝石 Semiconductor materials for IR Silicon 硅 Silver Bromide 溴化银 Silver Chloride 氯化银 Silver Halides Sodium Chloride 氯化钠 Thallous Halides X射线单色仪 Y3Al5O12 YAG YAG 钇铝石榴石 Zinc Selenide 硒化锌 Zinc Sulphide 硫化锌 切割成型胚料 原始晶粒 抛光光学元件 透射镜片 钇铝石榴石