Fiaxell SOFC氧化锆8YSZ、3YSZ、10YSZ电解质、电极和涂层
电解质
| Zirconia | Chemical formula | BET [m2/g] | D50 [µm] | Remarks |
| 8YSZ | 8mol.% (Y2O3)x(ZrO 2)1-x | 6.5 – 7.5 | 0.4 – 0.5 | for thin electrolytes |
| 3YSZ | 3mol.% (Y2O3)x(ZrO 2)1-x | 9 – 12 | 0.4 – 0.5 | for electrolyte substrate |
| 10YSZ | 10mol.% (Y2O3)x(ZrO 2)1-x | 0.3 – 0.7 | 11 – 13 | for decreasing the sintering activity |
| Ceria | Chemical formula | BET [m2/g] | D50 [µm] | Remarks |
| 10GDC | Gd0.1Ce0.9O1.95 | 10 – 13 | 0.1 – 0.2 | |
| 20GDC | Gd0.2Ce0.8O1.95 | 10 – 13 | 0.1 – 0.2 |  for composite cathode and buffer layer |
| SDC | Sm0.20Ce0.80O2-X | 12 – 14 | 0.1 – 0.2 | |
| Other dopants on request | ||||
Protonic conductors (BCY, BZY, BCZY are available on request
阳极
| Nickel oxide | Chemical formula | BET [m2/g] | D50 [µm] | Remarks |
| NiO | NiO | 6 – 8 | 0.6 – 0.7 | for electrodes and anode substrate |
阴极
| Cobaltite | Chemical formula | BET [m2/g] | D50 [µm] | Remarks |
| LSCF | (La0.60Sr0.40)0.95Co 0.20Fe0.80O3-X | 5 – 8 | 0.5 – 0.6 |  for active and composite layers |
| LSC | (La0.60Sr0.40)0.95CoO 3-X | 5 – 8 | 0.5 – 0.6 | for current collection, active and composite layers |
| Other compositions on request | ||||
| Manganite | Chemical formula | BET [m2/g] | D50 [µm] | Remarks |
| LSM | La0.5Sr0.3Mn1.05O 3 | 4 – 5 | 1.1 – 1.3 | for active and composite layers, compatible with YSZ electrolyte |
保护涂层
| Chemical formula | BET [m2/g] | D50 [µm] | Remarks | |
| CuMn2O4 | CuMn2O4 | 10 – 15 | 0.1 – 0.2 |  for interconnects under oxidizing atmosphere |
| Other compositions on request | ||||
孔隙度控制
| Chemical formula | BET [m2/g] | D50 [µm] | Remarks | |
| PMMA | Poly(methyl methacrylate) | 0.5 – 1 | 5 – 8 |  PMMA pore former to generate calibrated porosity in anode substrate or/and in electrodes |
| Other particle sizes on request | ||||