Capilla Schweissmaterialien GmbH是德国著名焊接产品品牌，成立于1959年，在全球焊接市场已有55年的经验，在全球40多个国家和地区拥有广泛的销售网络，Capilla公司从1966年就开始为自己的设备生产焊条，主要客户分布在建筑、锻造、采矿等行业。随着市场需求的扩大，Capilla开始延长产品线，生产高品质的焊材和焊接电极，在金属加工行业拥有1100多个合作伙伴，通过DIN EN ISO 9001:2008认证已超过十年，为用户提供高品质的焊接材料。主要产品包括：Capilla焊条、焊接耗材、焊接材料等欧美备件。
熔覆和堆焊用焊接耗材
1, 包覆和堆焊用涂覆棒电极
| capilla® | EN 14700 | DIN 8555 | Material no. | 应用区域 |
|---|---|---|---|---|
| 308 HL | E Fe 11 | E 8-UM-200 CKPR | 1.4316 | 1.4300, 1.4301, 1.4303, 1.4306, 1.4308, 1.4311, 1.4312, 1.4371, 1.4541, 1.4543, 1.4550, 1.4552 |
| 318 HL | E Fe 11 | E 8-UM-200 CKPR | 1.4576 | 1.4571, 1.4573, 1.4580, 1.4581, 1.4583, 1.4401, 1.4404, 1.4408, 1.4420, 1.4435, 1.4436 |
| 309 HL | E Fe 11 | E 8-UM-200 CKPR | ~1.4332 | 1.4541, 1.4550, 1.4710, 1.4712, 1.4727, 1.4729, 1.4740, 1.4742, 1.4780, 1.4825, 1.4826, 1.4828, 1.4878 |
| 51 W | E Fe 10 | E 8-UM-250 CKPR | 1.4370 | 1.3401 |
| 5201 | E Fe 11 | E 8-UM-250 CKPR | ~1.4459 | – |
| 52 | E Fe 11 | E 8-UM-300 CKPR | 1.4337 | 1.4762, 1.4085 |
| 56 | E Fe 9 | E 7-UM-200-K | 1.3402 | – |
| 56 Fe | E Fe 9 | E 7-UM-200-K | ~1.3402 | – |
| CR MA 47 | E Fe 9 | E7-UM-250-K | – | – |
| 250 B | E Fe 1 | E 1-UM-250 P | – | – |
| 300 B | E Fe 1 | E 1-UM-300 P | – | – |
| 400 B | E Fe 1 | E 1-UM-400 P | – | – |
| 500 B | E Fe 1 | E 1-UM-50 P | – | – |
| 54 W | E Fe 8 | E 6-UM-60 PS | ~1.4718 | – |
| 54-160 | E Fe 8 | E 6-UM-60 PS | ~1.4718 | – |
| 60 HRC | E Fe 15 | E 10-UM-60-GRZ | – | – |
| 540 | E Fe 15 | E 10-UM-65-GRZ | – | – |
| 540 SF | E Fe 15 | E 10-UM-65-GRZ | – | – |
| 540 Nb | E Fe 15 | E 10-UM-65-GRZ | – | – |
| 540 N | E Fe 16 | E 10-UM-65-TZ | – | – |
| 540 V | E Fe 16 | E 10-UM-65-TZ | – | – |
| 635 S | E Fe 15 | E 10-UM-65-Z | – | – |
| 68 HRC | E Fe 15 | E 10-UM-70-GCZ | – | – |
| 550 E | T Fe 20 | E 21-GF-UM-65 G | – | – |
| 550 G | T Fe 20 | G 21-GF-UM-65 G | – | – |
| 900 G | not classified | G 21-UM-65 G | – | – |
2， 包覆和堆焊用焊丝电极
2.1 包覆和堆焊层气体保护电弧焊用粗丝
| capilla® | EN 14700 | DIN 8555 |
|---|---|---|
| 5201 MAG | S Fe 10 | MSG 8-GZ-200 KPZ |
| 250 MAG | S Fe 1 | MSG 1-GZ-250 |
| 300 MAG | S Fe 1 | MSG 1-GZ-300 |
| 500 MAG | S Fe 1 | MSG 2-GZ-50 |
| 600 MAG | S Fe 8 | MSG 6-GZ-60 |
| 54 MAG | S Fe 8 | MSG 6-GZ-60 P |
| 655 MAG | S Fe 8 | MSG 6-GZ-60 GZ |
2.2包覆和堆焊用钨极惰性气体焊接用焊条
| capilla® | EN 14700 | DIN 8555 |
|---|---|---|
| 5201 WIG | S Fe 10 | MSG 8-GZ-200 KPZ |
| 250 WIG | S Fe 1 | MSG 1-GZ-250 |
| 300 WIG | S Fe 1 | MSG 1-GZ-300 |
| 500 WIG | S Fe 1 | MSG 2-GZ-50 |
| 600 WIG | S Fe 8 | MSG 6-GZ-60 |
| 54 WIG | S Fe 8 | MSG 6-GZ-60 P |
| 655 WIG | S Fe 8 | MSG 6-GZ-60 GZ |
2.3包覆和堆焊层气体保护电弧焊用管状焊丝
| capilla® | EN 14700 | DIN 8555 |
|---|---|---|
| G 350 MM | T Fe 1 | MF 1-GF-350 P |
| G 500 MM | T Fe 1 | MF 1-GF-50 GP |
| G 600 MM | T Fe 8 | MF 6-GF-60 GZ |
| G 600 Si MM | T Fe 8 | MF 6-GF-60 GZ |
| G 655 MM | T Fe 8 | MF 6-GF-60 GZ |
| 561 RLD | T Fe 9 | MF 7-GF-200/450 KPN |
| 562 RLD | T Fe 9 | MF 7–GF-200/450 KPN |
| 56 RLD | T Fe 9 | MF 7-GF-200/50 CKP |
| 52 RLD | T Fe 11 | MF 8-GF-150/400 KPZ |
| 5201 RLD | T Fe 10 | MF 8-GF-150/400 KPZ |
| 354 RLD | T Fe 14 | MF 10 GF-50 G |
| G 154 MM | T Fe 1 | MF 1-GF-40 P |
| G 254 MM | T Fe 1 | MF 1-GF-45 G |
| 5600 RLD | T Fe 9 | MF 7-GF-40 GKP |
| G54 MM | T Fe 8 | MF 6-GF-55 GP |
| G 54 N MM | T Fe 8 | MF 10-GF- 60 G |
| 55 RLD | T Fe 15 | MF 10-GF-60 G |
| 60 RLD | T Fe 15 | MF 10-GF-60 G |
| 540 RLD | T Fe 14 | MF 10-GF-60 CGT |
| 540 Nb RLD | T Fe 15 | MF10-GF-65-G |
| 540 N RLD | T Fe 16 | MF 10-GF-65 GT |
| 540 V RLD | T Fe 13 | MF 10-GF-65 GRZ |
| 540 B RLD | T Fe 13 | MF 10-GF-70 GRZ |
| 68 HRC RLD | T Fe 15 | MF 10-GF-70 GRZ |
| HR MAG | Special alloy | MF 21-GF-55 G |
| 911 G | Special alloy | MF 21-GF-65 G |
capilla® 308 HL
产品说明:
高复原金红石碱包覆焊条用于超低碳非稳定奥氏体不锈钢Cr-Ni钢的焊接，使用温度可达350℃，低温性能可低至-78℃。也适用于包覆非合金钢，这时要使用焊接缓冲层，推荐使用Capilla 309HL。
应用领域：
1.4300, 1.4301, 1.4303, 1.4306,
1.4308, 1.4311, 1.4312, 1.4371,
1.4541, 1.4543, 1.4550, 1.4552.
典型焊缝金属成分:
机械性能: (未经热处理;环境温度下的最小值)
尺寸：
还有以下相关型号：
Capilla 308 H
Capilla 308 KB
Capilla 308 L
Capilla 308 LR
Capilla 308 MAG
Capilla 308 WIG
Capilla G 308 L RM (管状丝)
capilla® 51 W
产品说明:
金红石基包覆高复原焊条，适用于异种接头的熔焊和低碳钢的包覆。
cr – ni – mn合金焊缝金属具有完全的奥氏体组织，可进行应变硬化。
在腐蚀性介质中的使用温度:高达300°C。
抗结垢:高达900°C。
应用领域：
不同铁素体-奥氏体接头的熔焊高含碳量的“难焊”钢的焊接，例如钢轨钢，应变硬化Mn钢的熔焊，例如X 120 Mn 12(1.3401)
耐磨堆焊的缓冲层。
典型焊缝金属成分:
机械性能: (未经热处理;环境温度下的最小值)
尺寸：
还有以下相关型号：
Capilla 51 Kb
Capilla 51 Ti
Capilla 51 MAG
Capilla 51 WIG
Capilla G 51 MM
Capicoat 51
capilla® 56
产品说明:
碱性涂层高回收棒电极。应变硬化焊缝金属是高锰合金。
适用于暴露在重冲击下的非常坚韧和耐磨的覆盖层的焊接，应采用低热量输入进行焊接。
应用领域：
用于因冲击和冲击而大量暴露于磨损的锰钢表面和零件的堆焊。
挖掘机齿、打臂、挖泥船螺栓、破碎机钳口及锥、喷砂及喷丸装置;铁路系统:交叉蛙和四向件。
典型焊缝金属成分:
机械性能: (未经热处理;环境温度下的最小值)
尺寸：
还有以下相关型号：
Capilla 561 RLD (管状丝)
capilla® 400 B
产品说明:
基本涂敷焊条，适用于机械易磨损部件的堆焊。焊条具有良好的焊接性能。采用交流电源。
适用于定位工作。渣很容易除去。
应用领域：
易受严重冲击和磨损的表面的敷焊硬合金层，例如。行走轮、土方机械、输送机螺丝、链斗输送机、导轨等。
覆盖层无裂纹。使用硬金属工具进行切削加工是可能的。
典型焊缝金属成分:
机械性能: (未经热处理;环境温度下的最小值)
尺寸：
capilla® 68 HRC
产品说明:
碱性石墨涂层高回收率焊条，适用于中等冲击下极耐磨覆盖层的焊接。
应用领域：
适用于暴露于矿石、黄铁矿、沙子、煤、水泥或炉渣造成的极端磨料磨损的非合金钢和合金钢构件的堆焊。
特别适用于煤、焦炭、矿渣破碎装置部件的装甲。
典型焊缝金属成分:
机械性能: (未经热处理;环境温度下的最小值)
尺寸：
还有以下相关型号：
Capilla 68 HRC RLD (管状丝)